搪瓷管的工作温度对自身使用的影响

为了能让大家更多的了解搪瓷管，下面给大家介绍搪瓷管的工作温度对自身使用的影响：

in order to let you know more about enamel pipe， the following to ioduce the work temperature of enamel pipe for their use:

搪瓷管经900℃高温焙烧，冷却后搪瓷与钢板粘结在一起。由于搪瓷的线膨胀系数和延伸率小于钢板，因此冷却后搪玻璃的变形量小于钢板的变形量，搪瓷受到钢板的约束产生压应力。搪瓷管制成后，其搪玻璃即存在预压缩应力，而钢板则存在预拉伸应力。

enamel tubes were calcined at high temperature after 900，&the cooling was bonded with the steel plate. because the enamel linear expansion coefficient&extension rate is less than the steel， so cooling after deformation of the glass lined smaller than that of the plate deformation， enamel is compressive stress caused by plate ctraint. after the cool of enamel， glass lining is pre compressive stress，&the steel plate are pre tensile stress.

由于预应力与线膨胀系数和延伸率相关，线膨胀系数和延伸率与温度又密切相关，因此搪瓷管的工作温度对搪瓷管的使用影响很大。如果因温度变化大而使搪瓷产生的应力超过其使用应力，搪瓷管空气预热器采购，搪瓷将被破坏。

as the prestressing force is related to linear expansion coefficient&elongation coefficient， linear expansion coefficient&extension rate are closely related to the temperature. enamel will be destroyed if the temperature changes greatly&the stress of the enamel is more than that of its use.

因此搪瓷管搪瓷层遇冷、热急变，极瓷。因此搪瓷管有耐温---：温度 200℃，耐温急变：冷冲击<1io~c，热冲击<120℃。投料时物料温度与罐体温差太大以及升温时蒸汽过猛、降温太急也能导致爆瓷。因此搪瓷管在使用中升、降温要缓慢、均匀，分级冷却。

therefore， the enamel enamel pipe cold hot blast， highly explosive porcelain. the enamel pipe with temperature resistant limit: 200 degrees celsius temperature，搪瓷管空气预热器多少钱， high temperature blast: cold shock <1io~c， heat shock <120 c. the temperature of the material&the tank temperature difference of the feed is too high&the heating steam， excessive cooling too quickly can also lead to explosive porcelain. therefore， in the use of enamel pipe/slow cooling， uniform cooling， grading.

如有需求欢迎来我公司选购，相信我们是您正确的选择！

if there is a need to welcome to our company to buy， believe that we are your best choice!

shanghai printing

搪瓷管酸洗气泡产生的原理

   酸洗气泡是因酸与的金属生成氢气所造成的。它在冷轧时会发出噼---的声，它的外观特征是呈条状的小鼓泡后呈黑色细裂缝。经过轧制后，气泡裂缝会延伸扩大致使搪瓷管产品的力学性能降低。

   搪瓷管酸洗气泡产生的机理是：金属和酸产生化学反应时生成了部分氢原子，它渗透到金属的结晶格子中，并使其变形变形后使氢更向金属内扩散，其中一部分氢原子穿过金属并分子化从酸液中逸出，部分氢原子的分子化在晶格变形产生的“显微空孔”边界上或搪瓷管的夹杂及孔隙中进行，氢在空孔中的压力可达到很大值使搪瓷管中产生了引起氢脆的内应力。防止搪瓷管产生气泡的措施是调整酸液的浓度；控制酸洗时溶液的温度和搪瓷管表面平直状态等。